What are the uses of enamel wire?

Precautions for storage should be well packaged, should not be placed in a high-humidity warehouse, should not be exposed to direct sunlight, and should not be placed near acids, alkalis and organic solvents.

The heat resistance class of enameled wire is the ambient temperature where the enameled wire can work normally for a long time (above 20000h).

List 5 type of enameled wire characteristics
Acetal enameled wire
Polyurethane enameled wire
Polyester and modified polyester enameled wire
Polyesterimide/polyamide imide composite enameled wire
Polyesterimide/polyamide composite enameled wire

ISO Certificated Polyimide Round Enamel Coated Magnet Wire has better performance than all other types of enameled wires. Polyimide paint film has only abrasion resistance slightly worse than polyester and polyvinyl acetal enameled wires. In order to improve this performance, most of the current Use polyester imide and polyamide imide to prepare enameled wire, which can increase the solid content of the paint, but the heat resistance is somewhat reduced.

1. Polyester enameled wire (P.E.W.)
Polyester enamel-covered wire is made of heat-resistant Terephthalic Polyester resin as the main grease as the insulating film and baked on the conductor. Its characteristics are as follows:
¡ñThe heat resistance is superior to synthetic tree (P.V.F.) enameled wire and U.E.W. enameled wire.
¡ñExcellent chemical resistance (except alkaline) and solvent resistance.
¡ñThe mechanical strength is comparable to synthetic resin (P.V.F.).
¡ñThe force rate and dielectric rate are comparable to U.E.W. enameled wire.
¡ñAlkali resistance and moisture resistance are better than synthetic resin enameled wire (P.V.F).

The multi-shaped enamel wire refers to a metal wire for winding electromagnetic coils with an insulating paint, also known as electromagnetic wires. The multi-shaped enameled wire is the primary raw material of electrical, motor and household appliances, telecommunications, electronic external electromagnetic windings. In the future, follow the rapid development of industrial appliances, household appliances, telecommunications, electronic products, etc. Market and application fields.

Brand Name: LP Magnet Wire
Certification: UL,SGS,RoHS,ISO9001
Conductor Material: copper or aluminum
Bobbin: 30kg/50kg/150kg wooden spool
Diameter: round:2.0-7.0; flat:a:1-10,b:3-35
Model Number: Paper Coated Copper Wire

1. Cutting
The enameled wire is composed of a conductor and an insulator, and the hardness of the two parts is very soft, so it can be cut by using a TabCUT-200 precision cutting machine with a general SiC cutting chip. Since the insulator is coated on the conductor, and its hardness and ductility are quite different, and the insulating layer has a certain degree of peeling, it is better to use some soft materials such as tin foil, rubber, etc. to wrap the cutting part when cutting. Up to prevent the insulation layer at the fracture from peeling off after cutting.

Telephone cable is usually thought of only as a communication medium operating at a normal 48 Vdc level. But telephone cable is regularly used by telephone operating companies to supply power to remote telephony equipment such as: PCM (Pulse Code Modulation) repeaters, FDM (Frequency Division Modulation) repeaters, telegraph and various types of control circuits. The normal talk battery voltage is regularly exceeded in the case of long subscriber loops utilizing loop extenders and on dial long line circuits which operate in the 70 to 100 Vdc range. For these applications, the referenced devices are generally current limited to approximately 150 milliamps. In all such cases, normal telephone industry practice usually limits pair-toground applied voltage to 150 Vdc, and pair-to-pair voltage is usually limited to 300 Vdc.

Thermal Class: 130-220C
Conductor Material: Copper
Standard: IEC,NEMA,GB,JIS
Delivery time: 7-30 Days
Brand Name: LP Magnet Wire
Insulation: PEW, PIW, EIW, AIW, EI/AIW

Three-layer insulated wire structure
High-frequency transformer triple-insulated wire is a high-performance insulated wire, so as the name suggests, this wire has three insulation layers with a core wire in the middle.
The first layer The first layer is golden yellow polyamine film, its thickness is a few microns, but it can withstand 3KV pulse high voltage
The second layer is a spray paint coating with high insulation,
The third layer is a transparent glass fiber layer. The total thickness of the insulating layer is only 20-100um. Its advantage is high insulation strength, and any two layers can withstand a safe voltage of 3000V AC, and the current density is large.

Best Price Factory Sale Enameled Copper Coated Aluminum Wire can be used at a working temperature of 180 ClassC. The product has the advantages of direct solderability, good coloring, and low dielectric loss under high frequency. Widely used in windings and wiring of motors, electrical appliances, electronic components, meters, etc.

What is called Magnet Wire? The magnetic wire is a copper wire with an enamel (a kind of paint ) coating on it, and used for transformer coils and motor coils. Copper wire is a conductor, like bare copper.

Enameled wire motors, electrical appliances, home appliances, communications, electronic information, instrumentation, power tools, automobiles and other industries provide supporting basic material industries. They are the main and key raw materials for electromagnetic windings of motors and electronic instruments. The rapid development of electronic products, etc., has brought a broader application field and market to enameled wires, but at the same time, higher requirements have been put forward for enameled wires, and enameled wires have continued to develop towards a high level and high quality.

Paper insulation enameled transposition conductor characteristics:
1. There is no circulating current, the eddy current loss in the coil is small, and the current density can be improved;
2. Simplify the winding process;
3. The full rate is higher than that of the paper-covered wire slot.

Paper-insulated enameled transposed wires are mainly used in the coils of large transformers.

The current enamel wire industry is relatively low due to the admission threshold, and therefore the production enterprises have more and more, and the market competition is constantly intensified, but in the high-end product field, there are not many companies that can enter, in the present, and future, The enamel wire business wants to achieve better development, and build brands and scale becomes more and more important.

The enameled wire manufacturer takes you to understand the high-temperature paint wrap of high-temperature paint wires, and it is necessary to judge, whether its appearance, size, and performance meet the technical standards of the product and user technical agreements. After the measurement, test, the technical standards of the product and the technical agreement of the product are compared to the requirements for qualified products, which does not meet the requirements for unqualified products.

Generally speaking, UL certified enameled wire needs to do four tests:
Thermal Aging Test (Full Thermal Aging Test or One Temperature Thermal Aging Test)
Dielectric Strength Test
Elongation and Heat Shock Test
Infrared Analysis – IR

Standards Of Enameled Wire includes
1）IEC 60317 for Europe
2）JIS C3202 for Asia
3）NEMA MW 1000C (inch) or NEMA MW 1000C metric (mm) for North America

The space factors of magnet wires are compared in the right figure. The space factors of enamelled wires are superior to those of other wires for winding, as are their electrical properties. However, more careful examination must be made of the following properties as compared with other wires.

Copper paint package wire production process principle

Copper lacquer wires are coated with respective lacquer solutions, and then cured by solvent volatilization and paint film.The earliest enamel wire is oily painted wire, made from tung oil.Its paint film is abrasion resistant, and cannot be used directly to make motor coils and windings, and the cotton yarn can be added to the layer.Later, polyethylene glycol formaldehyde lacquer wire came out, and its mechanical properties were greatly improved, which can be used directly for motor windings, which is called high-strength enameled wire.

Enameled Aluminum Wire Compared To Enameled Copper Wire have some advantages
Aluminum /Copper Wire/foils
Dimension:0.2–10.0mm,
Rectangular: A> 0.8–8mm, B> 2-22.5mm
Square: 0.4*0.4mm–8*8mm
Foils:Thickness：0.2–2.5mm, width:60–1250mm

Enameled wire
The insulation of enameled wire is varnish film, which is formed by coating insulating varnish on the conductive wire core and drying it.

Product features and uses
The paint film of the enameled wire is uniform and smooth, which is conducive to the automatic winding of the coil; the paint film is also thin, which is conducive to improving the space factor, and is widely used in small and medium-sized or micro electrical products

Glass-fiber covered aluminum magnet wire used to have weak coating strength (abrasion resistance, shock resistance, and flexibility). However, that disadvantage has been significantly improved recently by refining material selection and manufacturing methods. The demand for glass-fiber covered aluminum magnet wire is increasing as the wires have excellent uniformity and electrical properties under high temperatures and humidity.

Enameled wire is coated with insulating paint on the outside of the bare Aluminium wire, constitute the inside due to the effect of insulating varnish, between the two adjacent wire can bear 200 v ac voltage Q general insulation flow line surface light, soft, can work under the condition of 130 ¡æ continuous.In addition, enameled wire bending also requires 10 times, paint should not fall off, in order to meet the winding when won’t appear the quality problem.

Magnet Wire: enameled wire, winding wire, enamelled wire, magnetic wire, conductor covered
Type: copper winding wire, aluminum enameled wire
Application: motors, generators, transformers, and electric vehicles
Thermal Class: 130, 155, 180, 200, 220, 240

Fiberglass Covered Aluminum Wire Production Proce

One step :
Take the pure aluminum material drawing into the aluminium rod wire;

Two step :
Through the extrusion production line, take the aluminum rod wire into extruding and coarse drawing operation, then becoming the requirement specification of Bare aluminium wire;

Three step :
Take up the Bare aluminum wire conductor, and inspection the bare wire coil products;

Four step :
Annealing the bare aluminum wire, and placed neatly, ready to production;

Five step :
Pay-off the wire coil products, ready to fiber glass covering production;

Six step :
Taking into straightening and tension levelling operation, and then for the covering fiber glass;

Seven step :
Doing the fiber-glass covering operation, and inspecion the production process;

Eight step :
Packing the fiberglass covered wire products, and placed neatly in the warehouse.

Heat resistance refers to the properties of a substance that can maintain its excellent physical and mechanical properties under heated conditions. The highest use temperature of commonly used materials to characterize. There are different standards and test methods for different materials. Such as plastics are generally expressed by Martin heat-resistant temperature. The coating industry uses a blast constant temperature oven or a high temperature furnace. After it reaches the specified temperature and time, the surface condition of the paint film is inspected, tested, or other properties such as impact, bending, water immersion, salt spray test, etc., and then before and after Test data representation. All coatings used in higher temperature occasions must use heat resistance as an important technical indicator of the coating film

According to the characteristics and uses of insulation, winding wires can be divided into four categories: enameled wires, wrapped wires, special winding wires, and inorganic composite winding wires.

Enameled wire is a main type of magnet winding wire. It is composed of a conductor and an insulating layer. After the bare wire is softened by annealing, it is painted and baked many times. However, it is not easy to produce products that not only meet the requirements of the standard, but also meet the requirements of customers. It is affected by the quality of raw materials, process parameters, production equipment, environment and other factors. Therefore, the quality characteristics of various enameled wires are different, but they all have Mechanical properties, chemical properties, electrical properties, and thermal properties