UL approved enameled aluminum wire for motor

Winding wires used in electrical equipment are usually called magnetic wires. In other words, “magnetic wires are used to exchange electrical energy and magnetic energy.” Magnetic wire is roughly divided into enameled wire (insulation coated) and coated wire (fiber/film insulation) and their combinations. The two types of magnetic wires and their performance are very different. ASTM (American Society for Testing and Materials) B193, no more than 0.017241 ohm (square millimeter/meter), the film or coating should meet the latest version of ANSI, ASTM or NEMA applicable standards, and modify the specified resin. The modified resin is Chemically changed resin, or containing one or more additives to retain the basic chemical characteristics of the original resin to enhance certain performance or application characteristics, the coated conductor needs to meet all the required test requirements of the appropriate NEMA standard (UL certification project) .

Resistance:
Take 1m of the enameled wire to be inspected, scrape off the paint film at both ends, measure the resistance of the enameled wire, the resistance measurement value should be within the resistance range of GB/T6109; the standard temperature is 20 degrees, the conversion formula: 20 degrees resistance/234.5+standard Temperature = actual measured resistance/234.5 + measured temperature;

Enameled wire is coated with insulating paint on the outside of the bare Aluminium wire, constitute the inside due to the effect of insulating varnish, between the two adjacent wire can bear 200 v ac voltage Q general insulation flow line surface light, soft, can work under the condition of 130 ¡æ continuous.In addition, enameled wire bending also requires 10 times, paint should not fall off, in order to meet the winding when won’t appear the quality problem.

Compared with general round wires, flat enameled wires have the following advantages:
Higher floor area ratio and better use of space: The high conductor density enables coils and components of the same size to achieve higher efficiency, save materials and reduce costs.

Product Name:Oil Immersed Transformer Winding Wire
Type: round or rectangular wire
Features: Telephone paper, cable wire or 500KV transformer turn-to-turn insulation paper is used for insulation. After dipping.
Conductor Material:Aluminum or Copper
Application:used for Oil Immersed Transformer, transformer coils
Certificate:UL,RoHS
Thermal Class:105¡æ

The glass in Glass Fibre Conductor may be applied in woven tape form or as a continuous fibre. It has proved to be an efficient insulation providing coil winders with thermal stability, adequate electrical properties and good resistance to abrasion after varnishing. The glass is bonded with a varnish to improve dielectric strength and mechanical properties.

Copper-clad aluminum wire refers to a wire with aluminum core wire as the main body and a certain proportion of copper layer plated on the outside. It can be used as a conductor for coaxial cables and wire and cable conductors in electrical equipment. The aluminum wire has a small specific gravity, but its welding performance is not good. Therefore, the copper-clad aluminum wire is wrapped with a copper layer on the aluminum wire. This copper-clad aluminum wire can not only take advantage of the small aluminum specific gravity, but also improve the welding performance.

Advantages of oxide film wire
1. The oxide film is not sealed by insulating paint, and the temperature resistance can reach 250¡æ. The heat resistance of the oxide film sealed with insulating paint depends on the temperature index of the insulating paint;
2. High slot full rate, light weight and good radiation resistance.

For Aromatic polyimide tape-covered aluminum magnet wire, after the aluminum magnet wire is taped with a tape that is 1.5 mm thick with 1.0 mm of this thickness being polyimide film and the remaining 0.5 mm being fluoroplastic, it is heated and heat-sealed.

Paper insulation enameled transposition conductor characteristics:
1. There is no circulating current, the eddy current loss in the coil is small, and the current density can be improved;
2. Simplify the winding process;
3. The full rate is higher than that of the paper-covered wire slot.

Paper-insulated enameled transposed wires are mainly used in the coils of large transformers.

Application
? Oil-immersed transformer windings, Dry-type transformer, High temperature transformer,
? Motor, transformer, generator, welding machine; Sealed motor, Power tools motor, Auto alternators motor, Magnet coil, High power motor, household electro motors and micro-motors;
? Medium and large electrical motor and transformer windings;
? Power substations, rectifiers, f urnace transformer oil-immersed transformer coil winding;
? Lifting electromagnet, reactors and other low-voltage and high current electromagnetic winding;
? Used in aerospace, submersible motor and high voltage coil, wind turbines, micro-electronics and so on.
Windings with light weight, high conductivity, good heat resistance; Winding used for high frequency signal transmission
Magnetic wire used in High Frequency transformer, common transformer, inductance coils, electrometers.

The wrapped wire is made of natural silk, polyester fiber, glass fiber, insulating paper or synthetic resin film, etc., tightly wrapped on the conductive wire core to form an insulating layer. There are also insulating layers wrapped around the enameled wire. In addition to thin-film insulation, others such as glass filaments need to be dipped in adhesive insulating varnish to improve their electrical, mechanical and moisture-proof properties. In fact, they are combined insulation.

The paper covered wire is a type of enameled wire that is extruded or pulled by an oxygen-free copper rod or an electrical circular aluminum rod, and then annealing the wire, and then winding two layers or two layers of insulating on the copper (aluminum) conductor.Paper (including telephone paper, cable paper, high voltage cable paper, turns], suitable for oil immersion transformer coils and other similar electrical windings.Electrical bare copper (aluminum) wires produced by extrusion process are the most ideal materials for the production of cable paper wraps.

¡ñ Conductor resistance. Measure with a conductor resistance tester, and then change to the value at 20¡ãC for comparison.
¡ñInsulation destruction voltage. Twist two enameled wires, apply voltage between the conductors, and judge by the damage voltage of the paint film. This performance is analyzed and judged through two tests of normal state and cold state breakdown voltage.
¡ñPaint film continuity (pinhole). Check the small holes of the paint film with a certain length of the test material. The project is tested by a high-pressure paint film continuity tester.

Type of magnetic wire is divided into enameled wire, wrapping wire, insulated wire, combined wires and others,Mainly used in motors, electrical appliances, instruments, transformers, etc., to generate electromagnetic effects by winding coils, and use the principle of electromagnetic induction to achieve the purpose of converting electrical energy to magnetic energy

Telephone cable is usually thought of only as a communication medium operating at a normal 48 Vdc level. But telephone cable is regularly used by telephone operating companies to supply power to remote telephony equipment such as: PCM (Pulse Code Modulation) repeaters, FDM (Frequency Division Modulation) repeaters, telegraph and various types of control circuits. The normal talk battery voltage is regularly exceeded in the case of long subscriber loops utilizing loop extenders and on dial long line circuits which operate in the 70 to 100 Vdc range. For these applications, the referenced devices are generally current limited to approximately 150 milliamps. In all such cases, normal telephone industry practice usually limits pair-toground applied voltage to 150 Vdc, and pair-to-pair voltage is usually limited to 300 Vdc.

The selection criterion of the electromagnetic wire is not considered for resistance, as the problem of resistance and fever can be done by selecting the same cross-sectional wire, it is the main consideration of the thick wire or the thin wire is mainly considered Operability.

Enameled aluminum wire ,High resistance to heat shock, high temperature and good performace at softening breakdown, suitable for high-speed automated routing, able to be direct weld, with no pinhole, resistive to high frequency, wearing, refrigerants and electronics corona, high breakdown voltage

Polyimide Film Covered Aluminum Wire Production Process

One step :
Take the pure aluminum material drawing into the aluminium rod wire;
Two step :
Through the extrusion production line, take the aluminum rod wire into extruding and coarse drawing operation, then becoming the requirement specification of Bare aluminium wire;

Three step :
Take up the Bare aluminum wire conductor, and inspection the bare wire coil products;

Four step :
After annealing the alumium wire coil , cleaning and pay-off the wire coil, ready to next operation;

Five step :
Taking into straightening and Tension levelling operation, varnish treat the surface of wire, and then for the glass fiber covered;

Six step :
And then for baking the fiberglass wire , pulling the finished wire, and take-up the fiberglass wire products.

Paper covered wire by Electrical Aluminium Pole extrusion die by a certain size or drawn wire after annealing, and then in the aluminum conductor wrapped more than two or two insulating paper (including paper, telephone, cable paper, high voltage cable paper, turn insulation paper) of the winding wire, suitable for oil-immersed transformers and other electrical winding with a similar wire. Produced by the extrusion process electrical bare aluminum wire is wrapped production of the cable wire is the best material.

Anti-electricity-firecable wire
2. Aluminum winding wire
3. Three-layer extruded insulation wire

Paper Wrapped Aluminum wire Production Process

One step :
Take the pure aluminum material drawing into the aluminium rod wire;

Two step :
Through the extrusion production line, take the aluminum rod wire into extruding and coarse drawing operation, then becoming the requirement specification of Bare aluminium wire;

Three step :
Take up the Bare aluminum wire conductor, and inspection the bare wire coil products;

Four step :
Annealing the bare aluminum wire, and placed neatly, ready to production;

Five step :
Doing the digital dividing and cutting paper process and finished;
Pay-off the wire coil products, ready to paper covering production;

Six step :
Taking into straightening and tension lenvelling operation, ready to paper winding;

Seven step :
Taking into the paper winding operation, and then for inspecion;

Eight step :
Pulling the finished paper-covered wire, and then for take-up the wire coil , ready to packing.

UL Certificated 220 High Thermal Class Oxidized Film Aluminum Wire and aluminum strip insulated with aluminum oxide film are used in the fields of electronics, missiles, nuclear reactors, aerospace and aircraft industries. The oxide film has high flexibility and is suitable for winding electromagnetic coils of various shapes and sizes. The use of round or rectangular aluminum wires and aluminum strips can save 50% of metal, so it has commercial value. For example, linear motors and medical equipment industries are widely used because of their light weight and low inertia. For rotating equipment, light weight can simplify the dynamic balance, thus reducing the vibration generated by the dynamic balance, thereby improving the sensitivity of the moving coil and its high-frequency response.

The paint is a process of painting the paint of the enameled wire to form a uniform lacquer layer of a thickness on the metal conductor. This is related to several physical phenomena and painting methods of liquid.

Aromatic polyimide enameled wire has good heat resistance, softening breakdown resistance, radiation resistance, severe cold resistance and chemical resistance. Among them, many test indicators such as unidirectional scratching, breakdown voltage, and thermal softening are far Far better than ordinary enameled wire.

The enamel wire is a major variety of winding wires, composed of two conductors and insulating layers, after the naked wire is deck, and then painted, baked.However, it is not easy to produce products that meet the standard requirements, but also meet customer requirements, it is affected by factors such as raw materials, process parameters, production equipment, environment, and therefore, the quality characteristics of various enameled wires are different, but they haveFour major properties of mechanical properties, chemical properties, electrical properties, and thermal performance.

Application of China Factory Wholesale Copper Pianted Enameled Aluminum Wire
1. High frequency signal transmission
2. The preferred inner conductor material for cable television coaxial cable
3.50 RF cable, flexible RF coaxial cable inner conductor material
4. Leakage cable inner conductive material
5. Computer power supply, other data cable inner conductor material
6. Micro coaxial cable inner conductor material
7. Power transmission
8. Stranded wire
9. Power cable conductor material
10. Control cable inner conductor
11. Special cable inner conductor for automobiles and locomotives
12. Building non-wire conductor materials
13. Conductor materials such as bus bars
14. Fuse
15. Radio frequency shielding network.

Inductive sensors have outstanding advantages such as simple structure, fast dynamic response, and easy non-contact measurement. They are especially suitable for acids, alkalis, chlorides, organic solvents, liquid CO2, ammonia, PVC powder, ash, oil and water. Liquid level measurement such as interface is currently widely used in metallurgy, petroleum, chemical, coal, cement, food and other industries.

Fiberglass Covered Aluminum Wire Production Proce

One step :
Take the pure aluminum material drawing into the aluminium rod wire;

Two step :
Through the extrusion production line, take the aluminum rod wire into extruding and coarse drawing operation, then becoming the requirement specification of Bare aluminium wire;

Three step :
Take up the Bare aluminum wire conductor, and inspection the bare wire coil products;

Four step :
Annealing the bare aluminum wire, and placed neatly, ready to production;

Five step :
Pay-off the wire coil products, ready to fiber glass covering production;

Six step :
Taking into straightening and tension levelling operation, and then for the covering fiber glass;

Seven step :
Doing the fiber-glass covering operation, and inspecion the production process;

Eight step :
Packing the fiberglass covered wire products, and placed neatly in the warehouse.

1. Different materials: structure and composition are different
2. Different performance: Since the three-layer insulated wire cannot be directly welded, it needs to be stripped first, and the cost is higher, and it will be replaced by FIW; the insulation level is different, and the three-layer insulated wire can be produced with a temperature resistance of 200 degrees
3. Can be different in color, etc.